Tool steel
A6 Tool Steel
Manufacturer or standards-body identification; product values do not apply to every form or condition.
Identity / state reference
What distinguishes this material
The Carpenter A6 product has its own low-temperature air-hardening chemistry; it must not be identified as EN 1.2713/SKT4.
- Designation in this reference
- A6 / UNS T30106
- Forms covered by the sources
- Carpenter DeCarb-Free cold-finished rounds and flats.
- States to distinguish or confirm
- Annealed machining stock and final hardened/tempered tool are different states.
- Temperature and exposure
- No universal service-temperature limit or room-temperature property set is assigned. Use the cited product document and the purchase certificate.
Property evidence for a stated condition
No condition-specific numerical table is reproduced here
The linked sources establish the identity and the stated product/state scope. Obtain the row for your actual form, section, treatment and test conditions before adopting strength, hardness or a thermal limit.
Resolve these conditions next
- What product standard, edition and complete grade are on the material certificate?
- What product form, section size and delivery/heat-treatment condition will be machined?
For machining, take the exact grade, supplied condition and measured hardness where applicable into the tool maker’s application data. A generic material-family speed is not a substitute for an operation and tool-specific recommendation.
Sources and what they establish
Reviewed 23 October 2026. A source’s publication date and the review date are different. The scope below identifies the fields checked.
Carpenter A6 tool-steel datasheet
A6 / T30106 technical data; the URL folder name does not change this technical datasheet’s contents.
Carpenter A6 tool-steel datasheet ↗Source identity, a named product example and a supplied-batch certificate are different evidence. Cross-standard similarity does not approve substitution.
Corrections from the previous article
- Delete the incorrect 1.2713/SKT4 equivalence; use the actual A6 identity and treatment schedule.
- Withdraw the legacy generic hardness (217–241 HB (annealed)) and tensile-strength (1,860 MPa (270 ksi) hardened) pair: the old page does not establish a matching product, heat treatment, section and test source.
- Remove the unsupported cutting-speed table and machinability percentage; select tooling only after the actual material condition is known.