AISI 1010
Manufacturer or standards-body identification; product values do not apply to every form or condition.
Identity / state reference
What distinguishes this material
The Metallus 1010 chemistry row specifies carbon 0.08–0.13% and manganese 0.30–0.60% by mass. These identify the grade band; they are not a tensile-strength or hardness guarantee.
- Designation in this reference
- SAE 1010
- Forms covered by the sources
- Product form is not established by the Metallus chemistry table; obtain the supplier product specification.
- States to distinguish or confirm
- The chemistry designation does not establish a heat-treatment condition.
- Temperature and exposure
- No universal service-temperature limit or room-temperature property set is assigned. Use the cited product document and the purchase certificate.
Property evidence for a stated condition
No condition-specific numerical table is reproduced here
The linked sources establish the identity and the stated product/state scope. Obtain the row for your actual form, section, treatment and test conditions before adopting strength, hardness or a thermal limit.
Metallus Practical Data for Metallurgists, 19th edition (2024) ↗
Resolve these conditions next
- What product standard, edition and complete grade are on the material certificate?
- What product form, section size and delivery/heat-treatment condition will be machined?
For machining, take the exact grade, supplied condition and measured hardness where applicable into the tool maker’s application data. A generic material-family speed is not a substitute for an operation and tool-specific recommendation.
Sources and what they establish
Reviewed 23 October 2026. A source’s publication date and the review date are different. The scope below identifies the fields checked.
Metallus Practical Data for Metallurgists, 19th edition (2024)
Grade chemistry tables, printed pp. 4–7, visually checked; supports chemistry identity, not a universal mechanical-property or delivery-condition table.
Metallus Practical Data for Metallurgists, 19th edition (2024) ↗Source identity, a named product example and a supplied-batch certificate are different evidence. Cross-standard similarity does not approve substitution.
Corrections from the previous article
- Replace unqualified international equivalents with certificate-based comparisons; the reviewed chemistry source does not certify interchangeability.
- Withdraw the legacy generic hardness (105 HB) and tensile-strength (365 MPa (53 ksi)) pair: the old page does not establish a matching product, heat treatment, section and test source.
- Remove the unsupported cutting-speed table and machinability percentage; select tooling only after the actual material condition is known.